Influence of the operative parameters on chemical durability and rheological behavior of frits ceramic suspensions
57.zip Autori: F. Andreola, D. Bernardelli, M. Romagnoli, P. Pozzi
Presentato al: Southern Europe Conference on Rheology
Anno: 1999
Volume: 1 - Issue: Unico
Casa Editrice: SIR-Cuen Napoli
Lingua: English


Abstract
Glaze application is the phase in a productive process that is more conditioned from the rheological properties of the glaze itself. During the preparation step in the mill, at moderately high temperatures (60-70°C), reactions between frits and the aqueous medium can occur and consequently begin the leaching of glassy network and the diffusion of the modifying ions through the leached frit layer.
In the industrial process, variations on the pH and the ionic strength of glaze suspensions happen during the milling. Consequently changes on the rheological parameters (apparent viscosity, yield point, thixotropy) of glaze suspensions will verified. It is important to control these variables for keeping unaffected the aesthetic characteristics of the final products, after firing.

Attenzione la lettura completa dell'Abstract e il download dei file è riservata esclusivamente ai Soci dell'Associazione Italiana di Reologia.

Se sei un Socio ti preghiamo di effettuare il login se non lo hai già fatto

Nel caso non fossi un Socio dell'Associazione Italiana di Reologia ti preghiamo di visitare la sezione "Iscriviti all'Associazione" per procedere alla registrazione